Notum est, variae sunt notae vitreae et variae materiales classificationes, eorumque opera etiam variantur, quomodo eligat materiam ad ostentationem machinarum?
Vitreum operculum in crassitudine 0.5/0.7/1.1mm adhiberi solet, quae crassitudo schedae frequentissima in foro adhibetur.
Inprimis varias notas maioris vitri operculi inducamus;
1. US - Corning Felis Glass 3
Iaponia — Asahi Glass Dragontrail atq; AGC nitri vitrei calcis
3. Japan — NSG Glass
4. Germania — Schott Vitrum D263T vitrum borosilicum pellucidum
5. China - Dongxu Optoelectronics Panda Vitri
Sinis - South Glass Aluminosilicate Glass
7. Sina - XYG Maximum ferrum vitreum tenues
8. China - Caihong Aluminosilicate Vitri High
Inter eos, Vitrum Corning Gorilla optimum vulnus resistentia habet, durities superficies et qualitas superficiei vitreae, et sane pretium maximum.
Pro studio magis oeconomico jocus ad Corning materias vitreas, plerumque commendata domestica CaiHong alta aluminosailicate vitreum, non multam differentiam perficiendi habent, sed pretium esse potest circiter 30 ~ 40% vilis, variae magnitudinis, differentia etiam variabit.
Sequens tabula ostendit exhibitionem comparationis utriusque notae vitreae post temperantiam;
| Brand | Crassitudo | CS | DOL | Transmittance | Mollis Point |
| Corning Gorilla Glass3 | 0.55/0.7/0.85/1.1mm | ＞650mpa | 40um | ＞92% | DCCCC°C |
| AGC Dragontrail Glass | 0.55/0.7/1.1mm | ＞650mpa | 35um | ＞91% | 830°C |
| AGC Soda Lime Glass | 0.55/0.7/1.1mm | ＞450mpa | 8um | ＞89% | 740° C |
| NSG Glass | 0.55/0.7/1.1mm | ＞450mpa | 8~12um | ＞89% | 730°C |
| Schoot D2637T | 0.55mm | ＞350mpa | 8um | ＞91% | 733°C |
| Panda Glass | 0.55/0.7mm | ＞650mpa | 35um | ＞92% | 830°C |
| SG Glass | 0.55/0.7/1.1mm | ＞450mpa | 8~12um | -90% | 733°C |
| XYG Ultra Vitrum Serenum | 0.55/0.7//1.1mm | ＞450mpa | 8um | ＞89% | 725°C |
| CaiHong Vitri | 0.5/0.7/1.1mm | ＞650mpa | 35um | ＞91% | 830°C |
SAIDA dedicata semper vitreis nativus tradendis et praestandis servitiis maximae qualitatis et constantiae. Societates cum clientibus nostris aedificare studeas, consilia moventes a consilio, prototypo, per fabricam, cum cura et efficacia.