Vitrum borosilicatum expansionem thermalem minimam habet, fere unam ex tribus vitri sodae calcis. Compositiones principales approximatae sunt 59.6% arenae silicae, 21.5% oxidi borici, 14.4% oxidi kalii, 2.3% oxidi zinci, et vestigia oxidi calcii et oxidi aluminii.
Scisne quae aliae proprietates?
| Densitas | 2.30g/cm² |
| Duritia | Sex pedes |
| Modulus Elasticitatis | 67KNmm – 2 |
| Robur Tensilis | 40 – 120Nmm – 2 |
| Ratio Poissoniana | 0.18 |
| Coefficiens Expansionis Thermalis 20-400°C | (3.3)*10`-6 |
| Conductivitas Caloris Specifica 90°C | 1.2W*(M*K`-1) |
| Index Refractionis | 1.6375 |
| Calor Specificus | 830 J/KG |
| Punctum Liquefactionis | 1320°C |
| Punctum Mollitionis | 815°C |
| Impetus Thermalis | ≤350°C |
| Robur Impactus | ≥7J |
| Tolerantia Aquae | HGB 1级 HGB 1) |
| Acido Resistens | HGB 1级 HGB 1) |
| Resistentia Alcali | HGB 2级 HGB 2) |
| Proprietates Pressurae Resistentes | ≤10Mpa |
| Resistentia Voluminis | 1015Ωcm |
| Constans Dielectrica | 4.6 |
| Robur Dielectricum | 30 kV/mm |
Notum propter resistentiam caloris et durabilitatem physicam,vitrum borosilicatumin variis industriis et applicationibus adhibetur.
– Vitrea Laboratoria
— Tubi Vitrei Pharmaceutici
— Instrumenta Coquinaria et Instrumenta Culinae
— Instrumenta Optica
— Ornamentum Illuminans
— Pocula et cetera.
Saida Glass est peritaPROCESSIO VITRIOfficina per decem annos, inter decem officinas optimas numerari conamur, variis generibus rerum ad usum aptarum offerentibus.vitrum, sicut vitrum tegumentale ab 7'' ad 120'' pro quolibet ostentatione, tubi vitrei borosilicati 3.3 ab diametro externo minimo 5mm ad diametrum externom maximum 315mm.
Vitrum Saidaeconstanter nititur ut socius tuus fidus sit et te sentire sinat officia valoris additi.
Tempus publicationis: XIII Augusti MMXX