FAAMATALAGA
– 3.3 Coefficient o le fa'alauteleina o le vevela
- Tete'e maualuga o le vevela ma vaila'aumautu
–Super e tete'e masima & le susu & tete'e mu
–Mafolafola atoatoa ma lamolemole
–Fa'amautinoaga aso e tu'uina atu ai
–Feso'ota'iga tasi i le tasi ma ta'iala fa'apolofesa
–Fa'ailoga, lapopo'a, i'u ma le mamanu e mafai ona fa'atulagaina pe a mana'omia
–O lo'o maua le Anti-glare/anti-reflective/anti-fingerprint/anti-microbial iinei.
Lipoti o Mea Matata Matagofie Borosilicate
| 密度(Density) | 2.30g/cm² |
| 硬度(Mohs Malosi) | 6.0Mohs' |
| 弹性模量（Elasticity Modulus) | 67KNmm – 2 |
| 抗张强度(Malosi Tensile) | 40 – 120Nmm – 2 |
| 泊松比（Poisson ratio) | 0.18 |
| 热膨胀系数 （20-400°C）（Coefficient of Thermal Expansion) | (3.3)*10`-6 |
| 导热率比热（90°C）(Fa'asa'o ole vevela) | 1.2W*(M*K`-1) |
| 折射率（Fa'asino Upu) | 1.6375 |
| 比热（Avela Fa'apitoa) (J/KG) | 830 |
| 熔点（Ie Li'u) | 1320°C |
| 软化点（Fa'amaluluina) | 815°C |
| 连续工作温度/使用寿命（Fa'au'u Fa'agaoioi Temperature/Olaga Auaunaga) | 150°C |
| ≥120000h(-60°C-150°C) | 200°C |
| ≥90000h(-60°C-200°C) | 280°C |
| ≥620000h(-60°C-280°C) | 370°C |
| ≥30000h | 520°C |
| ≥130000h | |
| 抗热冲击（Thermal Shock) | ≤350°C |
| 抗冲击强度(Malosi A'afiaga) | ≥7J |
| 主要化学成分%含量（Main Chemical Composition % Content) | |
| SiO2 | 80.40% |
| Fe203 | 0.02% |
| Ti02 | 1.00% |
| B203 | 12.50% |
| Na20+K20 | 4.20% |
| FE | 0.02% |
| 耐水性（Faapalepale Vai) | HGB 1级 （HGB 1) |
O le a le tioata saogalemu?
O tioata fa'afefe po'o fa'ama'a'a o se ituaiga o tioata saogalemu e fa'agasolo ile fa'atonutonuina ole vevela po'o vaila'au e fa'ateleina
lona malosi pe a faatusatusa i tioata masani.
O le fa'avevesi e fa'apipi'i ai le pito i fafo ma fa'alavelave totonu.
VAAIGA AOAO
ASIASI MA FA'AALIGA
O MEA FA'AVAE uma e fa'aaogaina TAGATA I LE ROHS III (VISI EPA), ROHS II (VISI SINA), A'OA'O (VISI NEI)
O LE TATOU FAIGA
LA TATOU LAINA GAOGA MA LE Faleteuoloa
Lamianting ata puipui - Penina cotton afifi - Kraft pepa afifiina
3 ITIGA O FILIFILIGA TAPI
Lafoa'i atu i fafo pusa plywood - Fa'atau pepa fa'amomoli