Yakasiyana neGirazi reSoda-Lime Iyo yakajairwa chiyero ndeye 0.3 ~ 2mm, uye ikozvino kunewo 4mm, 5ml aluminosililiate girazi kusarudza kubva.
The theAnti-Glare GiraziOf The Bat panoridzwa nemakemikari etching maitiro anokwanisa kuderedza zvinokwanira glare yeratidziro yepamusoro, ichiita kuti mufananidzo wemufananidzo wakajeka uye unooneka unonyanya kujeka.
1. Hunhu hweEtached ag aluminoumson girazi
* Akanakisa anti-glare performance
* Low Flash Pfungwa
* Yakakwirira Tsanangudzo
* Anti-Fingerprint
* Kubata kwakasimba kunzwa
2. Saizi yegirazi
Inowanika Stickness Sarudzo: 0.3 ~ 5mm
Saizi yakakura iripo: 1300x1100mm
3..
* Gloss
Pa550nm wavelength, iyo yakakwira inogona kusvika 90%, uye inogona kugadziridzwa mukati mehukuru hwe78% ~ 90% maererano nezvinodiwa
* Transmittance
Pa550nm wavelength, kutapurirana kunogona kusvika 91%, uye kunogona kugadziridzwa muhuwandu hwe3% ~ 80% maererano nezvinodiwa
* Haze
Iyo shoma inogona kudzorwa mukati me3%, uye inogona kugadziridzwa mukati mehuwandu hwe3% ~ 80% maererano nezvinodiwa
* Roughness
Iyo shoma inotorwa 0.1um inogona kugadziridzwa mukati mehuwandu hwe0 # ~ 1.2m maererano nezvinodiwa
4. Zvivakwa zvemuviri zveEtached Ag aluminium silicon slab girazi
michina uye yemagetsi zvivakwa | Unit | Data |
Density | g / cm² | 2.46 ± 0.03 |
Inowedzera yekuwedzera inoenderana | x10△/ ° C | 99.0 ± 2 |
Sporing Inge | ° C | 833 ± 10 |
Innaling Pfungwa | ° C | 606 ± 10 |
Strain point | ° C | 560 ± 10 |
Mudiki's Modugus | GPA | 75.6 |
Shear Modulus | GPA | 30.7 |
Poisson Ratio | / | 0.23 |
Vickers kuomesa (mushure mekusimbisa) | HV | 700 |
Penzura kuomesa | / | > 7h |
Vhoriyumu kupesana | 1G (ω com) | 9.1 |
Dielectric nguva dzose | / | 8.2 |
Refractivation Index | / | 1.51 |
Photoalastic coefficient | NM / CM / MPA | 27.2 |
SEAS Girazi semakore gumi egirazi kugadzirisa gadzira, chinangwa kugadzirisa matambudziko ezvevatengi ekukunda-kuhwina kushandira pamwe. Kuti udzidze zvakawanda, taura zvakanakanyanzvi yekutengesa.
Kutumira Nguva: Jan-10-2023