Ukwethulwa kwe-AG Aluminium-Silicon Glass

Okuhlukile kwingilazi ye-soda-lime, ingilazi e-aluminilisicate inokuguquguquka okuphakeme, ukumelana kokusakaza, ukugoba amandla namandla okulawula, futhi kusetshenziswa amaphaneli okulawula, futhi kusetshenziswa amaphaneli wegeyimu, imikhiqizo ye-3c nezinye izinkambu. Ubukhulu obujwayelekile bungu-0.3 ~ 2mm, futhi manje kukhona futhi ingilazi engu-4mm, 5mm i-aluminililate ongakhetha kuyo.

Le khasiingilazi elwa nengilaziIphaneli yokuthinta esetshenziswe yinqubo yamakhemikhali etching inganciphisa ngempumelelo ukugqama kwezimpawu eziphezulu, okwenza ikhwalithi yesithombe icace futhi umphumela obonakalayo ubhekane namaqiniso ngokweqiniso.

  ingilazi ye-aluminilicate ngephrinta

1. Izici ze-Etched AG Aluminiumon Glass

* Ukusebenza okuhle kakhulu kwe-anti-glare

* Iphuzu eliphansi le-flash

* Incazelo ephezulu

* Anti-Fingerprint

* Ukuxhumana okunethezekile zizwe

 

2. Usayizi wengilazi

Izinketho Zokubukhali Okutholakalayo: 0.3 ~ 5mm

Usayizi omkhulu otholakalayo: 1300x1100mm

 

I-3. Izakhiwo ze-Optical ze-Etched AG Aluminium Silicon Glass

* Vala gloss

Ku-at 550nm waveghth, inani eliphakeme lingafinyelela kuma-90%, futhi lingashintshwa ngaphakathi kwebanga lama-75% ~ 90% ngokuya ngezidingo

* Ukudluliselwa

Ngo-550nm waveghth, ukudluliselwa kungafinyelela ama-91%, futhi kungashintshwa ebangeni lama-3% ~ 80% ngokuya ngezidingo

* Haze

Ubuncane bungalawulwa kungakapheli ama-3%, futhi bungashintshwa ngaphakathi kwebanga le-3% ~ 80% ngokuya ngezidingo

* Ubulukhuni

Ukulawulwa okuncane kwe-0.1um kungashintshwa ngaphakathi kwebanga le-0. ~ 1.2um ngokuya ngezidingo

 

4. Izakhiwo ezibonakalayo ze-Aluminium Alumin Aluminium Slab Glass

Izakhiwo ezenziwa ngogesi nezakagesi

Umuvo

Umbhalo

Incekusana

g / cm²

2.46 ± 0.03

Ukunwebeka okwenziwe nge-thermal

I-X10/ ° C

99.0 ± 2

Iphuzu lokuthambisa

° C

833 ± 10

Iphuzu lokukhulisa

° C

606 ± 10

I-Strain Point

° C

I-560 ± 10

I-modulus Young

Uhlobo

75.6

I-Shear modulus

Uhlobo

30.7

Isilinganiso sikaPoisson

/

0.23

Ubulukhuni be-Vickers (ngemuva kokuqiniswa)

HV

I-700

Ubulukhuni bepensela

/

> 7h

Ukumelana ngevolumu

I-1G (ω · cm)

9.1

Dielectric njalo

/

8.2

Inkomba ye-Refuac

/

1.51

I-Photelastic Coefficient

NM / CM / MPA

27.2

I-SayA Glass njengeminyaka eyishumi ukucubungula ingilazi ukukhiqiza, okuhlose ukuxazulula izinkinga zamakhasimende ukubambisana win-win. Ukuze ufunde kabanzi, thintana ngokukhululeka kwethuUkuthengiswa kwesazi.